Modeling and Investigation of the Swelling Kinetics of Acrylamide-Sodium Acrylate Hydrogel


Creative Commons License

KIPÇAK A. S., İSMAİL O., DOYMAZ İ., Piskin S.

JOURNAL OF CHEMISTRY, 2014 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Basım Tarihi: 2014
  • Doi Numarası: 10.1155/2014/281063
  • Dergi Adı: JOURNAL OF CHEMISTRY
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Yıldız Teknik Üniversitesi Adresli: Evet

Özet

The acrylamide-sodium acrylate hydrogel was synthesized by free radical polymerization of the method of solution polymerization. Dynamic swelling tests were conducted at 25, 40, and 60 degrees C temperatures, in order to investigate the swelling properties of the synthesized hydrogel. The results have shown that swelling content and swelling rate of the hydrogel increase with increasing the swelling water temperature. The diffusivity values changed from 1.81 x 10(-7) to 2.97 x 10(-7) m(2) s(-1) over the temperature range. The activation energies were found as 3.56, 3.71, and 3.86 kJ mol(-1) at 25, 40, and 60 degrees C, respectively. The experimental drying curves obtained were fitted to a three different models, namely, Peleg's, first-order absorption kinetic, and exponential association equation models. All the models applied provided a good agreement with the experimental data with high values of the coefficient of determination (R-2), the least values of the reduced chi-square (chi(2)), and root mean square error (RMSE). Comparing the determination of coefficient, reduced chi-square, and root mean square error values of three models, it was concluded that the exponential association equation model represents swelling characteristics better than the others.