Reciprocal dry sliding wear behaviour of B4Cp reinforced aluminium alloy matrix composites


Creative Commons License

Toptan F., Kerti I., Rocha L. A.

WEAR, cilt.290, ss.74-85, 2012 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 290
  • Basım Tarihi: 2012
  • Doi Numarası: 10.1016/j.wear.2012.05.007
  • Dergi Adı: WEAR
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.74-85
  • Yıldız Teknik Üniversitesi Adresli: Evet

Özet

In the present work, AlSi9Cu3Mg alloy matrix composites reinforced with 15 and 19 vol% B4Cp were produced by squeeze casting route at 850 degrees C under low vacuum. Titanium-containing flux (K2TiF6) was used to promote the wetting between B4C and liquid aluminium metal. It was found, from the microstructural observations, that the wetting improved by the formation of a thin Ti-rich reaction layer. In order to investigate the wear properties, the samples were subjected to reciprocating wear tests against AISI 4140 pin under dry sliding conditions. The effect of B4C volume fraction, sliding velocity, applied load and sliding distance on reciprocal dry wear behaviour of composites was studied using general full factorial experimental design. The effects of factors and interactions on the coefficient of friction (COF) and the wear rate values of both composite specimens and counter materials were studied. Worn surfaces and wear debris were characterised using field emission gun scanning electron microscope (FEG-SEM), Energy Dispersive X-Ray Spectroscopy (EDS), optical microscope (OM) and X-Ray diffraction (XRD). From microstructural investigations, wear mechanism was suggested as a combination of adhesive, abrasive, and delamination wear. (C) 2012 Elsevier BM. All rights reserved.