Magnesium borates are one of the major groups of boron minerals that have good neutron shielding performance. In this study, dehydrated magnesium borates were synthesized by solid-state method using magnesium oxide (MgO) and boron oxide (B2O3), in order to test their ability of neutron shielding. After synthesizing the dehydrated magnesium borates, characterizations were done by X-ray Diffraction (XRD), fourier transform infrared (FT-IR), Raman spectroscopy, and scanning electron microscopy (SEM). Also boron oxide (B2O3) contents and reaction yields (%) were calculated. XRD results showed that seven different types of dehydrated magnesium borates were synthesized. 1000 degrees C reaction temperature, 240 minutes of reaction time, and 3 : 2, 1 : 1 mole ratios of products were selected and tested for neutron transmission. Also reaction yields were calculated between 84 and 88% for the 3 : 2 mole ratio products. The neutron transmission experiments revealed that the 3 : 2 mole ratio of MgO to B2O3 neutron transmission results (0.618-0.655) was better than the ratio of 1 : 1 (0.772-0.843).