The linear relationship between compressive strength and ultrasonic velocity in castable refractories

---

Atıf İçin Kopyala

Yaman C., Abkan T., Akdogan A.

EURO CERAMICS VIII, PTS 1-3, ss.1823-1826, 2004 (SCI-Expanded)

• Yayın Türü: Makale / Tam Makale
• Basım Tarihi: 2004
• Doi Numarası: 10.4028/www.scientific.net/kem.264-268.1823
• Dergi Adı: EURO CERAMICS VIII, PTS 1-3
• Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED)
• Sayfa Sayıları: ss.1823-1826
• Yıldız Teknik Üniversitesi Adresli: Evet

Özet

In this experimental work, castable refractory has been used. In pressing the water percent was in the range of 7.5-9.5 % weight, and the seven cylindrical specimens for each mixture have been pressed under 4000 N/cm(2) into a steel mould. In casting the water percent was in the range of 10-12 % weight. After mixing castable with water, the specimens, which contain more than 9.5 % water, have been casted to 40 x 40 x 40 mm(3) into a steel mold by vibrating.