Effect of modifying agents on the hydrophobicity and yield of zinc borate synthesized by zinc oxide


Acarali N. B. , Bardakci M., TUĞRUL N. , Derun E. , Piskin S.

INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, cilt.20, ss.574-581, 2013 (SCI İndekslerine Giren Dergi)

  • Cilt numarası: 20 Konu: 6
  • Basım Tarihi: 2013
  • Doi Numarası: 10.1007/s12613-013-0768-6
  • Dergi Adı: INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS
  • Sayfa Sayısı: ss.574-581

Özet

The aim of this study was to synthesize zinc borate using zinc oxide, reference boric acid, and reference zinc borate (reference ZB) as the seed, and to investigate the effects of modifying agents and reaction parameters on the hydrophobicity and yield, respectively. The reaction parameters include reaction time (1-5 h), reactant ratio (H3BO3/ZnO by mass: 2-5), seed ratio (seed crystal/(H3BO3+ZnO) by mass: 0-2wt%), reaction temperature (50-120A degrees C), cooling temperature (10-80A degrees C), and stirring rate (400-700 r/min); the modifying agents involve propylene glycol (PG, 0-6wt%), kerosene (1wt%-6wt%), and oleic acid (OA, 1wt%-6wt%) with solvents (isopropyl alcohol (IPA), ethanol, and methanol). The results of reaction yield obtained from either magnetically or mechanically stirred systems were compared. Zinc borate produced was characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), and contact angle tests to identify the hydrophobicity. In conclusion, zinc borate is synthesized successfully under the optimized reaction conditions, and the different modifying agents with various solvents affect the hydrophobicity of zinc borate.