Investigation of directional solidified Al-Ti alloy


KAYA H., CADIRLI E., Boyuk U., Marasli N.

JOURNAL OF NON-CRYSTALLINE SOLIDS, vol.355, pp.1231-1239, 2009 (Journal Indexed in SCI) identifier identifier

  • Publication Type: Article / Article
  • Volume: 355
  • Publication Date: 2009
  • Doi Number: 10.1016/j.jnoncrysol.2009.05.008
  • Title of Journal : JOURNAL OF NON-CRYSTALLINE SOLIDS
  • Page Numbers: pp.1231-1239

Abstract

Al-1 wt% Ti alloy was directionally solidified upwards under argon atmosphere under the two conditions; with different temperature gradients (G = 2.20-5.82 K/mm) at a constant growth rate (V = 8.30 mu m/s) and with different growth rates (V = 8.30-498.60 mu m/s) at a constant temperature gradient (G = 5.82 K/mm) in a Bridgman furnace. The dependence of characteristic microstructure parameters such as primary dendrite arm spacing (lambda(1)), secondary dendrite arm spacing (lambda(2)), dendrite tip radius (R) and mushy zone depth (d) on the velocity of crystal growth and the temperature gradient were determined by using a linear regression analysis. A detailed analysis of microstructure development with models of dendritic solidification and with previous similar experimental works on dendritic growth for binary alloys were also made. (C) 2009 Elsevier B.V. All rights reserved.