Ultrafine Carbide-Free Bainite in High-Carbon Steel After Continuous Annealing with Different Cooling Rates
Journal of Materials Engineering and Performance, cilt.32, sa.11, ss.4922-4931, 2023 (SCI-Expanded, Scopus)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 32 Sayı: 11
- Basım Tarihi: 2023
- Doi Numarası: 10.1007/s11665-022-07446-4
- Dergi Adı: Journal of Materials Engineering and Performance
- Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, PASCAL, Aerospace Database, Applied Science & Technology Source, Aquatic Science & Fisheries Abstracts (ASFA), Chemical Abstracts Core, Communication Abstracts, Compendex, Computer & Applied Sciences, INSPEC, Metadex, Civil Engineering Abstracts
- Sayfa Sayıları: ss.4922-4931
- Anahtar Kelimeler: carbide-free bainite, continuous annealing, fracture toughness, heat treatment, microstructure, steel
- Yıldız Teknik Üniversitesi Adresli: Hayır
Özet
In addition to conventional isothermal heat treatment, ultrafine carbide-free bainite can be obtained by continuous annealing of steels, which is of great interest to scientists and research communities. The resulting microstructure consists of bainitic sheaves composed of bainitic ferrites interwoven with austenite films in nanoscale, being separated by austenite microblocks resulting in GPa-strength level. This article aims to investigate the microstructural characteristics and impact toughness of high-carbon steel after continuous cooling heat treatment at cooling rates of 0.1, 0.15, 0.2 and 0.3 °C/min. Results indicated that bainitic ferrites and austenite films of less than 270 nm and different volume fractions of bainitic sheaves and high carbon retained austenite could be attained. Wider size distribution of bainitic ferrites was achieved by a slower cooling rate due to the progressive transformation of the primary austenite to bainite. Finally, it has been shown that impact toughness values were increased by decreasing the cooling rate of the steel due to a more effective TRIP effect and obtaining more bainitic sheaves with different orientations, while premature bainite transformation and the presence of martensite deteriorated the impact toughness when the highest cooling rate was applied.