Sonochemical Synthesis of Copper Borates: Effect of Reaction Conditions on the Characteristic Properties
Journal of the Turkish Chemical Society, Section A: Chemistry, cilt.11, sa.2, ss.461-466, 2024 (Scopus, TRDizin)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 11 Sayı: 2
- Basım Tarihi: 2024
- Doi Numarası: 10.18596/jotcsa.1342058
- Dergi Adı: Journal of the Turkish Chemical Society, Section A: Chemistry
- Derginin Tarandığı İndeksler: Scopus, TR DİZİN (ULAKBİM)
- Sayfa Sayıları: ss.461-466
- Anahtar Kelimeler: Borate, Copper, SEM, Spectroscopy, Ultrasound, X-ray methods
- Yıldız Teknik Üniversitesi Adresli: Evet
Özet
The effect of ultrasonic treatment on liquid-state production and the characteristic features of synthesized powder were studied in liquid-state conditions. In sonochemical synthesis, the operation parameters of mole ratio, reaction temperature, and time were optimized. The synthesis was achieved in moderate conditions such as mole ratio of copper: sodium: boron (Cu: Na: B) 1:2:1, 70°C and 2.5 minutes. The prepared samples were identified as copper borate (Cu(BO2)2) with the powder diffraction file number "00-001-0472". The reaction yields were also increased from 50% to 71.5% with the modification of the experimental procedure. The specific FT-IR peaks were observed at 1090, 985, 872, 781 and 731 cm-1 band values. In the morphological analyses, the agglomerations of multi-angular particles were seen. The results showed the affirmative effects of the possible use of the ultrasonic treatment on both the practical synthesis and the increase of characteristics.