Structural Modification of Sol-Gel Synthesized V2O5 and TiO2 Thin Films with/without Erbium Doping
ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2014 (SCI-Expanded, Scopus)
- Yayın Türü: Makale / Tam Makale
- Basım Tarihi: 2014
- Doi Numarası: 10.1155/2014/795384
- Dergi Adı: ADVANCES IN MATERIALS SCIENCE AND ENGINEERING
- Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
- Açık Arşiv Koleksiyonu: AVESİS Açık Erişim Koleksiyonu
- Yıldız Teknik Üniversitesi Adresli: Evet
Özet
Comparative work of with/without erbium- (Er-) doped vanadium pentoxide (V2O5) and titanium dioxide (TiO2) thin films were carried out via sol-gel technique by dissolving erbium (III) nitrate pentahydrate (Er(NO3)(3)center dot 5H(2)O) in vanadium (V) oxoisopropoxide (OV[OCH(CH3)(2)](3)) and titanium (IV) isopropoxide (Ti[OCH(CH3)(2)](4)). Effect of Er doping was traced by Fourier transform IR (FTIR), thermogravimetric/differential thermal (TG/DTA), and photoluminescence measurements. UV-Vis transmission/absorption measurement indicated a blue shift upon Er doping in V2O5 film due to the softening of V=O bond while appearance of typical absorption peaks in Er-doped TiO2 film. Granule size of the films increased (reduced) upon Er substitution on host material compared to undoped V2O5 and TiO2 films, respectively.