Corrosion Behaviour of Al/(TiB2 + -Al3Ti)-Based Functional Grade Metal Matrix Composite by Sedimentation Method

Kocaman E., Aydın H., Yiğit K., Çalışkan F., Savaş Ö.

Transactions of the Indian Institute of Metals, cilt.77, sa.8, ss.2153-2161, 2024 (SCI-Expanded) identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 77 Sayı: 8
  • Basım Tarihi: 2024
  • Doi Numarası: 10.1007/s12666-024-03301-3
  • Dergi Adı: Transactions of the Indian Institute of Metals
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Aerospace Database, Communication Abstracts, INSPEC, Metadex, Civil Engineering Abstracts
  • Sayfa Sayıları: ss.2153-2161
  • Anahtar Kelimeler: Aluminium composites, Corrosion, Functionally graded materials, Intermetallic, Sedimentation
  • Yıldız Teknik Üniversitesi Adresli: Evet

Özet

The current study examined the producibility and corrosion behaviour of functionally graded Alm/Al3Ti and TiB2 composites by sedimentation method. For this aim, the Al-Ti-B master alloy melted at 800 ℃ in the crucible and kept for 90 min to ensure the sedimentation of Al3Ti and TiB2 particles. In the samples taken from different sections of the crucible via a top-down approach, it was observed that the sedimentation method is rather suitable for obtaining of FGM composite. In the Rietveld analyses conducted across the sections for the refinement of crystal structures, it was determined that the amount of particles increased from top to bottom. Corrosion tests performed in different NaCl concentrations showed that the particle fraction did not have a direct effect on the corrosion resistance of the layers. Also, the highest corrosion resistance was obtained in the D layer without particle reinforcement, corrosion resistance decreased with particle reinforcement. Graphical Abstract: (Figure presented.).