Formation of macroporous poly(acrylamide) hydrogels in DMSO/water mixture: Transition from cryogelation to phase separation copolymerization

Ozmen M. M., Okay O.

REACTIVE & FUNCTIONAL POLYMERS, vol.68, no.10, pp.1467-1475, 2008 (SCI-Expanded) identifier identifier


Poly(acrylamide) hydrogels were prepared by free-radical crosslinking copolymerization of acrylamide and N,N'-methylenebis(acrylamide) at -18 degrees C in aqueous DMSO solutions of various composition. The hydrogels formed in the solvent mixture with less than 25% DMSO by volume have irregular large pores of about 10(1) mu m in diameter, typical for macroporous networks created by the cryogelation technique. Non-porous hydrogels were obtained in solutions containing 25% DMSO, while at larger DMSO contents, the structure of the hydrogel networks consists of aggregates of microspheres, which looks as cauliflowers, typical for a macroporous network formed by reaction-induced phase separation mechanism. Swelling measurements show that fast responsive PAAm hydrogels can be obtained as the DMSO content in the mixed solvent is decreased or increased starting from 25 v/v%. The results were interpreted as the transition from cryogelation to the phase separation copolymerization due to the marked freezing point depression of the solvent mixture as well as due to the action of the mixed solvent as a poor solvating diluent at -18 degrees C. It was also shown that the initial temperature of the cryogelation reactions in water strongly affects the hydrogel properties. Hydrogels formed at an initial temperature T-ini of 0 degrees C were very tough and can be compressed up to about 100% strain without any crack development while those formed at T-ini = 21 degrees C were fragile. (C) 2008 Elsevier Ltd. All rights reserved.