Dry sliding wear of Ni alloyed austempered ductile iron
China Foundry, cilt.13, sa.5, ss.361-367, 2016 (SCI-Expanded, Scopus)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 13 Sayı: 5
- Basım Tarihi: 2016
- Doi Numarası: 10.1007/s41230-016-6072-0
- Dergi Adı: China Foundry
- Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
- Sayfa Sayıları: ss.361-367
- Anahtar Kelimeler: Ausferrite, Austempered ductile iron, Austenite, Nickel, Wear
- Açık Arşiv Koleksiyonu: AVESİS Açık Erişim Koleksiyonu
- Yıldız Teknik Üniversitesi Adresli: Hayır
Özet
Measurements of dry sliding wear are presented for ductile irons with composition Fe-3.56C-2.67Si- 0.25Mo-0.5Cu and Ni contents of 0.8 and 1.5 in wt.% with applied loads of 50,100 and 150 N for austempering temperatures of 270,320,and 370 °C after austenitizing at 870 °C for 120 min. The mechanical property measurements show that the grades of the ASTM 897M: 1990 Standard can be satisfied for the selected austempering conditions. The results show that wear resistance is independent of austempering temperature with an applied load of 50 N,but there is a strong dependence at higher austempering temperatures with applied loads of 100 and 150 N. Observations indicate that wear is due to subsurface fatigue with cracks nucleated at deformed graphite nodules.